Dacrylate High Performance Metal Coatings
Dacrylate High Solids Polyurethane

Dacrylate High Solids Polyurethane

Reference No.: 85-Line

Acrylic modified polyurethane coating typically used for the long term protection of galvanising, steel and similar.

Fully compliant to Environmental Protection Act (1990) as required by Guidance Note PG 6/23 (97), Clause 20(d), and conforms to Highways Agency Specification (Item 168).

Colours available: Full range to special order, please contact us for full details. Dacmix scheme available for all British Standard and RAL colours.
Appearance Of Dried Film: High gloss
Volume Solids: 57%
Dry Film Thickness: Typical 50 microns / Range 40-70 microns
Theoretical Coverage: 11.4m² per litre at 50 microns
Drying Time At 20°C:
Touch Dry: 2 hours
Film Dry: 6 hours
Overcoat: N/A
(will vary with temperature, air movements, etc.)
V.O.C.: 390 gram/litre
Packaging: 5 litre composite packs
Shelf Life: 2 years or longer in unopened containers when stored under cover in good storage conditions.
Storage: Under cover with temperature range of 5°C to 32°C.
Surface Preparation: Normally applied over Dacrylate Epidac 2 primers and Epidac 2 MIO or Highways Agency Item 111 and 112.
Application Conditions: Humidity: Do not apply at relative humidities above 90%. Substrate temperature must be at least 3°C above dew point.
Temperature: Do not apply at temperatures below 5°C.

 

Dacrylate HS Polyurethane will cure at temperatures down to 0°C, however at tempertures below 15°C, the base and hardener will thicken considerably and affect application characteristics. At low ambient temperatures we would advise that base and hardener are warmed separately to 20°C before use to ensure optimum applicatin properties.

    Effect of Temperatures on Drying/Overcoating Times
    5°C 10°C 20°C 30°C
  Surface Dry 6 hours 4 hours 2 hours 1 hour
  Hard Dry 16 hours 12 hours 8 hours 4 hours
Overcoating Times Minimum 16 hours 12 hours 8 hours 4 hours
Maximum --- --- --- ---

 

Application: By brush or airless spray.
Airless Spray: 2500psi (170 bar)
Tip Size: 13-15 Thou (0.33-0.38mm)
Apply at an approximate wet film thickness of 90 microns to achieve dry film thickness of 50 microns.
Pot Life (at 20°C): 4 Hours
Mixing ratio by volume: 4 parts base to 1 part activator
Clean-up: Dacrylate Thinner R6.
Health and Safety: For more information request relevant Material Safety Datasheet.

 

Certain products retain solvents for longer periods, which will affect plasticizers within the plastic packaging causing damage to the finish. It is therefore not recommended that finished painted products be wrapped in bubble wrap, plastic sleeves, or similar, until coatings are fully cured as this can cause damage to the finish especially when stacked or stored in sunlight/elevated temperatures.

Damage can also occur from condensation caused by fluctuations in temperature consequently causing a 'greenhouse' effet within the packaging.

Polychromatic colours such as RAL 9006 and RAL 9007 may be susceptible to slight variations in colour depending on application methods and the type of paint. In order to obtain the best colour and appearance, these colours are best spray applied.

The above information is general information on the product but without warranty. Since conditions of service and application are beyond our control we cannot accept claims for loss, damage etc., based on this information. Dacrylate will not accept any claim for consequential or incidental damages.